Lactone stabilizing compositions

ABSTRACT

This invention provides a novel class of compounds and compositions and synthetic methods related to lactone antioxidant 3-arylbenzofuranones. The compounds may be useful to prevent yellowing and deterioration of organic materials preferably polymers, such as polyurethane foams as one example. The lactone antioxidants may be polymeric, and may also be liquid or paste in physical form at room temperature. Although it is not necessary for its stabilizing properties, the compositions may, in some species, bear one or more reactive primary OH groups on the polymer chains. The chains may also contain oligomeric oxyalkylene ether and aliphatic ester functional groups, in one embodiment of the invention.

FIELD OF THE INVENTION

The present invention relates to compositions comprising an organic material, such as a polymer, and an oligomeric lactone for use as a stabilizers. The inventive compositions may be employed for stabilization of organic materials against oxidative, thermal, or light-induced degradation. The invention is directed to novel oligomeric lactones.

BACKGROUND OF THE INVENTION

Various compositions are known that function to stabilize organic materials against oxidative, thermal or light-induced degradation. Such stabilization compositions may have broad applications in thermoplastics such as polyolefin, thermoset resins such as polyurethanes, and coating formulations. One problem with polyurethane foams, for example, is that such foams tend to yellow after a certain period of time. Yellowing of foam products is undesirable. Such yellowing may be caused by NOx gas fading or UV radiation.

U.S. Pat. Nos. 4,325,863 and 4,338,244 to Hinsken disclose 3-aryl benzofuran-2-ones and their dimers as new class of stabilizers in various organic polymers such as polyolefins, polyurethanes and polyesters.

U.S. Pat. Nos. 5,367,008 and 5,369,159 and 5,428,162 to Nesvadba disclose the preparation of various 3-(alkoxyphenyl)benzofuran-2-ones and 3-(acyloxyphenyl)benzofuran-2-one derivatives, for use as polymer stabilizers.

The prior art provides a number of relatively non-reactive, solid stabilizers. Solids are difficult to use in manufacturing processes. Solids provide difficulties in handling, migration, fogging, and blooming.

New and more effective stabilizing compounds are needed in the industry. This invention provides such compounds.

DETAILED DESCRIPTION OF THE INVENTION

Reference now will be made to the embodiments of the invention, one or more examples of which are set forth below. Each example is provided by way of explanation of the invention, not as a limitation of the invention. In fact, it will be apparent to those skilled in the art that various modifications and variations can be made in this invention without departing from the scope or spirit of the invention.

This invention provides a novel class of compounds and compositions and synthetic methods. In one aspect of the invention, the compositions may comprise polymeric or oligomeric lactone antioxidants, such as poly(oxyalkylene) chain(s) substituted 3-arylbenzofuranones or poly(caprolactone) chain(s) substituted 3-arylbenzofuranones. The inventive lactone antioxidants may be polymeric or oligomeric, which may be liquid or pastes in nature at room temperature. In many applications, liquid or paste forms of such compounds provide a remarkable and surprising advantage. Although it may not be necessary for its stabilizing properties, the compositions may bear one or more reactive primary —OH groups on the polymer chains. For some applications, the terminal group(s) of the polymer chain(s) is not believed to be critical with regard to the functioning of the polymeric lactones in stabilizer compositions. The chain(s) may also contain oxyalkylene ether and aliphatic ester functional groups or radicals.

The inventive liquid lacones polymeric/oligomeric chains may contain oxyalkylene segments (such as ethylene oxide and/or propylene oxide, etc, and the EO/PO ratio can be designed as such to achieve desired hydrophilic and/or hydrophobic properties) and/or aliphatic ester segments (hydrophobic). This affords the opportunity to “tune” the lactone antioxidants for desirable compatibility in various media such as thermosets (polyurethane), thermoplastics (PET, PP, PS, PC and the like), wax, aqueous systems (liquid hand soap, detergents, sunscreens, fabric softeners etc. consumer products), and coatings.

Lactones bearing unique polymeric/oligomeric chains may also be comprised of specific combination of EO/PO/aliphatic esters that are compatible with most of the above-mentioned applications. The liquid nature of the inventive polymeric lactones provides ease of handling during the application process. That is, the compositions may desirably be liquids or pastes at room temperature, making it much easier to apply the compositions in manufacturing processes. And the polymeric/oligomeric nature of the inventive lactones provides higher molecular weight and better compatibility with application media, thus is less volatile, and less prone to migrate, bloom and plate-out.

In some applications, primary hydroxy groups are present on the inventive lactone molecules. These structures offer superior reactivity in polyurethane, PET and coating systems. Thus the polymeric lactone molecules may be chemically attached on to the application media if such is desirable. The inventive polymeric UV absorbers may solve or mitigate migration, leaching, fogging, plate-out, and extraction problems, each of which is highly undesirable.

The inventive polymeric lactone antioxidants 3-arylbenzofuranones, when used along with other additives such as UV absorbers, other antioxidants, and light stabilizers, may significantly reduce the gas fading (NOx) and UV radiation induced yellowing of white polyurethane foam. The compositions may be provided in liquid form, and are reactive into the foam, which is a significant advantage. That is, these compositions are truly polymeric or oligomeric, having in some applications polyoxyalkylene and aliphatic polyester block copolymer/oligomer chains.

The inventive lactone stabilizers may be liquid and polymeric. They may provide ease of handling, processing and metering. The inventive lactone stabilizers may bear primary —OH groups at the end of polymer chains. They may be completely reactive in polyurethane, coatings, PET, and polycarbonate applications if such is desirable. They may provide antioxidant functions to resist undesirable extraction, migration, fogging, and leaching out of the polymer matrix.

In one application, the compounds of the invention may be described as follows:

wherein:

R₁-R₈ are each independently selected from the group consisting of:

-   -   H, F, Cl, Br, I, C₁-C₂₀ alkyls, C₁-C₂₀ cycloalkyls, C₁-C₂₀         alkoxy groups, C₇-C₂₀ phenylalkyls, and phenyl groups;

A comprises a C₂-C₂₀ alkyl group or a divalent oligomeric oxyalkylene radical;

Z comprises a C₂-C₂₀ alkyl or a divalent oligomeric ester radical; and

G is an end group and is selected from the group consisting of:

-   -   H, C₁-C₁₀ alkyls, alkyl carbonyls and aryl carbonyls.

The composition “A” recited above may comprise a divalent oligomeric oxyalkylene radical, which may provide the structure:

wherein:

EO comprises ethylene oxide or a derivative thereof;

PO comprises propylene oxide or a derivative thereof;

R₉ comprises a divalent C₁-C₂₀ alkyl radical;

x, y and w are independently selected from the group consisting of: zero and positive integers or fractions between 1 and 20; wherein

x+y+w is equal or greater than 1; and wherein

R₁₀ comprises H or a C₁-C₂₀ alkyl group.

Furthermore, the Z group may be comprised of a divalent oligomeric ester radical, having the structure:

wherein:

R₁₁ and R₁₂ are independently selected from H or C₁-C₁₀ alkyl groups;

n comprises an integer between 1 and 10; and

m comprises any positive integer or fraction between 1 and 20.

In another embodiment, a compound of the invention may also be represented by the formula:

wherein R1, R3, R5-R8, A, Z and G are as defined above.

Still in another embodiment, a compound of the invention may also be represented by the formula:

wherein:

-   -   R₁, and R₃ are as defined above, and     -   q is a positive integer between 1 and 20, and     -   t is a positive integer between 0 and 20, and wherein q+t is         equal to or greater than 3.

Further specifically, a compound of the invention may be represented by the formula:

wherein q and t are as defined above.

The compounds according to the invention may be effective antioxidants when used alone or in combination with other conventional antioxidants, for stabilizing organic materials, for example for coatings and a large number of polymers. For all applications in which a liquid, oligomeric and non-migration properties are highly desirable, the inventive compounds afford advantages over conventional lactone antioxidants. These polymers may be polyurethane, polyolefin, polycarbonate, polyamide, epoxyl resin, polyethers such as polyethylene glycol, polypropylene glycol or polytetramethylene glycol, and the like.

The stabilizing compositions are incorporated into the organic material by the conventional methods, for example in any desired phase during the manufacture of shaped products. They can, for example, be mixed in the form of a liquid, a paste, a powder with other materials, suspensions or emulsions or solutions into the polymer, which can be in the form of a powder, melt, solution, suspension or emulsion.

In stabilizing polyurethane foam in particular, the inventive compounds can be used with the following classes of additives:

Class A: Benzotriazoles are (in general) those compounds that conform to the structure represented as the following:

wherein R₁₃, R₁₄, and R₁₅ are independently selected from hydrogen, a group having a formula C_(a)H_(b)N_(c)O_(d)S_(e) wherein a, b, c, d, and e are from 0 to 30, and halogen.

Class B: Hindered phenols or BHT derivatives, and related compounds typically conform to the structure of the following:

wherein R₁₆ is selected from the group consisting of hydrogen, a group having a formula C_(a)H_(b)N_(c)O_(d)S_(e) wherein a, b, c, d, and e may be from 0 to 30, and halogen.

Class C: Secondary diphenylamines may conform to the structure of the following

wherein R₁₇ and R₁₈ are individually selected from the group consisting of hydrogen, a group having a formula C_(a)H_(b)N_(c)O_(d)S_(e) wherein a, b, c, d, and e are from 0 to 30, and halogen.

Class D: other conventional Lactone-based antioxidants may include those compounds that conform to the structure of the following:

wherein R₁₉ to R₂₇ are individually selected from the group consisting of hydrogen, a group having a formula C_(a)H_(b)N_(c)O_(d)S_(e) wherein a, b, c, d, and e are from 0 to 30, and halogen.

Several examples of the synthesis and application of the invention are shown below, in written form of Examples, and in data produced for Tables.

Synthetic Examples of the Invention Example 1

Two hundred seventy four grams of 2,4-di-tert-butylphenol, 165 g of 4-hydroxymandelic acid and 530 ml of acetic acid were combined in a two liter three neck round bottom flask equipped with a temperature probe, stirring apparatus and condenser. The mixture was heated to 95° C., at which, 2.6 g of methanesulfonic acid were added. The reaction was allowed to proceed at 95° C. for three hours. After cooling to room temperature and sitting overnight, the precipitated product was collected via filtration. This filtercake was washed several times with acetic acid until the precipitate was white. After drying in a 50° C. oven, 175 g of 5,7-di-tert-butyl-3-(4-hydroxyphenyl)benzofuran-2-one product having a melting point of 189-191° C. were obtained.

Example 2

In a three liter three neck round bottom flask, a solution of 32.4 g of sodium hydroxide in 810 ml of water was formed. With stirring, 91.6 g of 5,7-di-tert-butyl-3-(4-hydroxyphenyl)benzofuran-2-one were added and the mixture heated to 80° C. under a nitrogen atmosphere. Once at 80° C., 27 ml of 2-chloroethanol were added and the reaction held at 80° C. for two hours. After cooling to room temperature, a solution of 99 ml of concentrated hydrochloric acid in 1251 ml of water was added and the reaction held again at 80° C. for an additional hour. Once cooled to room temperature, the liquid was decanted and the remaining solid dissolved in 500 ml of methylene chloride. This solution was washed once with 300 ml of water. After drying the methylene chloride layer over magnesium sulfate and stripping, 92.6 g of 5,7-di-tert-butyl-3-[4-(2-hydroxy-ethoxy)-phenyl]benzofuran-2-one, a light yellow solid remained. This solid can be further recrystallized from ethanol/water.

Example 3

Fifteen grams of 5,7-di-tert-butyl-3-[4-(2-hydroxy-ethoxy)-phenyl]benzofuran-2-one, 13.5 g of ε-caprolactone and 0.3 g of 50% hypophosphorous acid were charged to a 100 ml three neck flask. Under a nitrogen atmosphere, the mixture was heated to 100° C. and held for three hours. Twenty four grams of viscous liquid product having a light yellow color were obtained.

Example 4

Three hundred grams of 5,7-di-tert-butyl-3-(4-hydroxyphenyl)benzofuran-2-one, 500 g of toluene and 3 g of lanthanum phosphate catalyst were charged into an autoclave. The reaction mixture was purged several times with nitrogen gas (to a pressure of 60 PSIG) and finally pressurized to 5 PSIG of nitrogen. After heating the autoclave to 121° C., ethylene oxide was added to the reaction mixture until the pressure in the reactor reached 60 PSIG. After the pressure dropped to 30 PSIG due to consumption of ethylene oxide, more ethylene oxide was added to the reactor in the same fashion as previously described until a total of 192 g of ethylene oxide had been added. Afterwards, the reaction mixture was post-cooked for a total of 30 minutes. Toluene was removed via vacuum stripping yielding 472 g (96%) of a light yellow viscous liquid.

Article Production and Performance Testing for Inventive Liquid Polymeric Lactone Antioxidants a) Polyether Foam Article Formation

-   -   The inventive lactone antioxidants were incorporated with or         without other additives to produce (in one particular embodiment         of the invention) polyurethane foam in accordance with the         following formulation and procedure:

Component Amount F3022 Polyol (from Bayer)  100 grams Water 4.53 ml DABCO 33LV (catalyst, from Air Products) 0.15 ml DABCO T10 (catalyst) 0.32 ml L520 Silicone (from Crompton)  1.0 mL 80/20 Toluene diisocyanate (Bayer, 112 index) 49.0 ml Reactint ® Blue X3LV as noted Inventive Polymeric Lactone Antioxidants as noted Additive from Class A as noted Tinuvin ® 326 Additive from Class B as noted Irganox ® 1135 Additive from Class C as noted Irganox ® 5057 Additive from Class D as noted Irganox ® HP 136

Upon mixture within a reaction vessel, the reaction created a “health” bubble (indicating gelation and blowing balance), and the vessel was then exposed to 160° C. (generated within a conventional oven to simulate actual heat history encountered on an industrial production level) for about 3 minutes allowing the material to cure to form a foam bun. The resultant foam buns were then analyzed for performance, as discussed in details below.

b) Performance Characteristics of Polyether Foams Including Inventive Polymeric Liquid Lactone Antioxidants

-   -   The white foams made in accordance with formulation and process         as described in Section a), were all tested for standard foam         performance, in terms of rise time, tack time, and bun height,         and compared with the control polyether foams either made with         conventional commercial lactone antioxidant Irganox® HP 136 or         made without additive. Measurements within 5% of the control are         considered acceptable for the finished foam product. The         measurements are summarized in Table 1.

TABLE 1 Foam Performance of Inventive or Comparative Lactone Antioxidants Sample Additive Loading Rise Time Tack Time Bun Height Foam # (Mw) (php) (minutes) (minutes) (mm) A1 N/A N/A 1.50 3 226 A2 HP-136 1.0 1.54 3 230 (Mw 350.7) A3 Example 3 1.0 1.52 3 234 (Mw 724) A4 Example 3 2.0 1.52 3 228 (Mw 724) A5 Example 4 1.0 1.50 3 232 (Mw 558) A6 Example 4 1.6 1.55 3 233 (Mw 558)

Additionally, the foams produced exhibited good resiliency and densities measured at about 1.5 pounds per cubit foot. Thus, the inventive polymeric lactone antioxidants provide acceptable polyurethane foam articles as compared with control samples.

c) Extraction Measurements From Polyurethane Foams

-   -   The polyurethane foams produced in above Section b) were         analyzed for extraction levels using the following method. The         extraction test involved cutting 1 gram of the cured foam from         the center of the sample and post-curing the cut foam for         another 20 minutes at 160° C. in a glass jar. After cooling to         room temperature, 75 grams of methanol were then added to the         glass jar that was then capped for 1 hour. The foam was then         removed and the extract solution was analyzed to detect the         percentages of the lactone antioxidants being extracted out. The         results are summarized in Table 2.

TABLE 2 Foam Extraction Tests of Inventive or Comparative Lactone Antioxidants Sample Additive Loading Extraction Foam # (Mw) (php) (%) A1 N/A N/A Not detectable A2 HP-136 1.0 >96 (Mw 350.7) A3 Example 3 1.0 <5 (Mw 724) A4 Example 3 2.1 <5 (Mw 724) A5 Example 4 1.0 <5 (Mw 558) A6 Example 4 1.6 <5 (Mw 558)

Based on the molecular weight of these additives, 1.0 php of HP-136 is molar equivalent to 2.1 php of inventive additive from Example 3, and 1.6 php of inventive additive from Example 4. As suggested from Table 2, the inventive liquid polymeric lactone antioxidants provide significant improvement in the foam extraction test, comparing to comparative examples such as commercial product HP-136.

d) Protection of Colorants from Thermal Discoloration in Polyurethane Foam

-   -   Liquid polymeric colorant Reactint® Blue X3LV (available from         Milliken Chemical) is widely used for the coloration of         polyurethane foam, and is known to be prone to thermal         discoloration during foam article formulation. Thus, the blue         foams were made in the presence of 1 php Blue X3LV with or         without inventive and comparative lactone antioxidants, in         accordance with formulation and process similar to those as         described Section a), with the exception that after the reaction         created a “health” bubble (indicating gelation and blowing         balance), the vessel was then exposed to 185° C. (generated         within a microwave oven to simulate actual heat history         encountered on a large industrial production environment) for         about 10 min before it was exposed to 160° C. (generated by a         conventional oven) for 3 minutes to cure the foam bun. The foam         buns were sliced in half, and then compared reading at the         center of the foam bun (usually where the discoloration occurs)         in CMC for delta E with the reading at the outer section of the         foam bun (usually where no discoloration occurs). The results         are summarized in Table 3.

TABLE 3 Stabilize Reactint ® Blue X3LV from Thermal Discoloration during Polyurethane Foam Formation Sample Loading Observation at the Foam # Additive Mw (php) Delta E center of foam bun A7 Control n/a n/a 4.6 some yellowing or (X3LV only) color loss A8 HP-136 350 1 1.8 No color change A9 Example 3 724 1 1.9 No color change A10 Example 4 558 1 2.4 Trace yellowing or color loss A11 Example 4 558 1.5 1.4 No color change

The data in Table 3 suggested that the inventive polymeric liquid lactone antioxidants were very effective in stabilization of polymeric colorants such as Blue X3LV from thermal degradation during the polyurethane foam production process.

e) Protection of Pure Polyol from Thermal Degradation/Yellowing During Polyurethane Foam Formation

-   -   Polyols are known to be very prone to oxidation. In order to         retain the physical and chemical properties, almost all         commercial polyols are protected with conventional hindered         phenol antioxidants for storage and transportation. One major         side effect of the hindered phenols is that they cause         discoloration/yellowing during polyurethane article formation         and when exposed to exhaust gas (NOx). An antioxidant which can         effectively protect the intergraty of polyols without causing         polymers such as polyurethane foam yellowing and compatible with         polyols is highly desired. In order to test the effectiveness of         the inventive polymeric lactone antioxidants, the white foams         (without adding any colorant) were made using pure polyol (no         conventional antioxidant package presence) with or without         inventive and comparative lactone antioxidants, in accordance         with formulation and process similar to those as described         Section a), with the exception that after the reaction created a         “health” bubble (indicating gelation and blowing balance), the         vessel was then exposed to 185° C. (generated within a microwave         oven to simulate actual heat history encountered on a large         industrial production environment) for about 10 min before it         was exposed to 160° C. (generated by a conventional oven) for 3         minutes to cure the foam bun. The foam buns were sliced in half,         and then compared reading at the center of the foam bun (usually         where the discoloration occurs) in CMC for delta E with the         reading at the outer section of the foam bun (usually where no         discoloration occurs). The results are summarized in Table 4.

TABLE 4 Performance of Compositions in Stabilizing Pure Polyol from Thermal Degradation/Yellowing During PU Foam Formation Sample Loading Observation at the Foam # Additive Mw (php) Delta E foam center A12 Control n/a n/a 48.1 Very yellow (Pure polyol) A13 HP-136 350 0.1 1.1 No color change A14 HP-136 350 1 4.2 No color change A15 Example 3 724 0.1 1.5 No color change A16 Example 3 724 1 2.3 No color change A17 Example 4 558 0.1 2.6 No color change A18 Example 4 558 1 2.8 No color change

Thus, the inventive polymeric liquid lactone antioxidants are very effective in stabilizing pure polyols from thermal degradation.

f) Protection of Polyurethane Foam Made with Pure Polyols from Gas Fading

-   -   In order to test the effectiveness of the inventive polymeric         lactone antioxidants in stabilizing the pure polyols from gas         (NOx) fading and comparing the performance with commonly used         conventional hindered phenol antioxidant package, the white         foams (without adding any colorant) were made using pure polyol         (no conventional antioxidant package presence), as well as         regular polyols (with the conventional stabilizer package         presences) with or without inventive and comparative lactone         antioxidants, in accordance with formulation and process similar         to those as described in Section a). After curing, the foam buns         were sliced in half, and small pieces of foam samples (diameters         of 10 cm×5 cm×2 cm) were cut from the center of each foam bun.         These foam samples were all tested under NOx gas chamber (NOx         concentration is 1 ppm) for discoloration at different exposure         time. Those foam samples exposed to different amounts of time in         NOx chamber testing were then compared reading in CMC for delta         E with respected unexposed foam samples. The results are         summarized in Table 5.

TABLE 5 Performance of Compositions in Stabilizing PU Foam Formation Made with Pure Polyol from Gas Fading Observation of Sample Loading exposed foam Foam # Additive Mw (php) Delta E sample A19 Control 1 n/a n/a 39.4 Yellow-brownish (regular polyol) A20 Control 2 n/a n/a 13.4 Slight yellow (Pure polyol) A21 HP-136 350 0.1 21.5 Slight yellow A22 Example 3 724 0.1 16.7 Slight yellow A23 Example 4 558 0.1 17.1 Slight yellow A24 Example 4 558 0.4 17.5 Slight yellow

It is thus clear that the inventive liquid polymeric lactone antioxidants are superior to conventional hindered phenol antioxidant package in stabilizing polyol from NOx fading.

g) Reduction of Discoloration in White Polyurethane Foam

-   -   Several white foams made in accordance with formulation and         process as described in Section a), in the presence of unique         anti-discoloration additive packages consists of a UV absorber         selected from Class A, a phenolic antioxidant from Class B, a         secondary amine antioxidant from Class C and a lactone         antioxidant from Class D. The inventive liquid polymeric lactone         antioxidants are used in this unique additive package to replace         the commercial antioxidant Irgnox® HP-136 which is solid and/or         may not thoroughly miscible with polyols. The foams are made         with the inventive additive packages, as well as commercially         available additive packages, the foam buns are then sliced in         half and 2 sets of small pieces of foam samples (diameters of 10         cm×5 cm×2 cm) were cut from the center of each foam bun. One set         of these foam samples were tested under Xenon lamp and compared         the performance against UV discoloration (Xenon lamp test         according to AATCC Test No. 16-1999) and Another set of samples         were tested under NOx gas chamber (NOx concentration is 1 ppm)         for discoloration at different exposure time (gas fading test as         described in AATCC Test No. 23-1999). Those foam samples exposed         to different amounts of time under UV lamp or in the NOx chamber         were then compared reading in CMC for delta E with respected         unexposed foam samples. The inventive synergistic additive         composition packages are listed in Table 6. Also included in         Table 6 as comparatives, are control (with no additive) and         commercially available additive packages B-75 (Ciba), CS-31         (Crompton) and LS-1 (Ortegol), which are current best commercial         products in polyurethane industry for stabilization of white         polyurethane foams.

TABLE 6 Additive Compositions and Loadings in Foam Formulation Additive Class A Class B Class C Lactone AO package (php) (php) (php) (php) AA Tinuvin 326 Irgnox 1135 Irgnox 5057 HP-136 (1.5) (0.33) (0.50) (0.57) BB Tinuvin 326 Irgnox 1135 Irgnox 5057 Example 3 (1.5) (0.33) (0.50) (1.18) CC Tinuvin 326 Irgnox 1135 Irgnox 5057 Example 4 (1.5) (0.33) (0.50) (0.57) DD Tinuvin 326 Irgnox 1135 Irgnox 5057 Example 4 (1.5) (0.33) (0.50) (1.16) GG Tinuvin B75 (commercially available from Ciba), loading @ 3.0 php HH CS-31 (commercially available from Crompton), loading @ 3.0 php JJ LS-1 (commercially available from Goldschmidt), loading @ 3.0 php Control 0 0 0 0

Lightfastness and gas fade test results for the inventive and comparative sample foams are summarized in Table 7.

TABLE 7 Test Results for Inventive and Comparative Additive Packages Lightfastness Gas Fade Gas Fade Sample Additive delta E delta E delta E Foam # Package (13 hrs) (2 hrs) (4 hrs) A25 Control (N/A) 34.6 34.2 56.2 A26 AA 8.7 8.8 21.2 A27 BB 7.7 10.8 27.6 A28 CC 11.6 11.8 33.4 A29 DD 10.0 11.3 23.5 A30 GG 15.8 34.1 82.5 A31 HH 18.2 51.4 53.1 A32 JJ 13.5 37.3 53.6

Clearly, the inventive additive packages containing the inventive liquid polymeric lactone antioxidants exhibited among the best overall performance against discoloration of UV exposure and gas fade, comparing to state-of-the-art commercial additive packages such as GG, HH and JJ.

It is understood by one of ordinary skill in the art that the present discussion is a description of exemplary embodiments only, and is not intended as limiting the broader aspects of the present invention. The invention is shown by example in the appended claims. 

1. A compound having the structural formula:

wherein: R₁-R₈ are independently selected from the group consisting of: H, F, Cl, Br, I, C₁-C₂₀ alkyls, C₁-C₂₀ cycloalkyls, C₁-C₂₀ alkoxy groups, C₇-C₂₀ phenylalkyls, and phenyl groups; A comprises a C₂-C₂₀ alkyl group or a divalent oligomeric oxyalkylene radical; Z comprises a C₂-C₂₀ alkyl or a divalent oligomeric ester radical; and G comprises an end group selected from the group consisting of: H, C₁-C₁₀ alkyls, alkyl carbonyls and aryl carbonyls.
 2. The compound of claim 1 wherein said A comprises a divalent oligomeric oxyalkylene radical having the structure:

wherein: EO comprises ethylene oxide or a derivative thereof; PO comprises propylene oxide or a derivative thereof; R₉ comprises a divalent C₁-C₂₀ alkyl radical; x, y and w are independently selected from the group consisting of: zero and positive integers or fractions between 1 and 20; the sum of x+y+w is equal to or greater than 1; and R₁₀ comprises either H or a C₁-C₂₀ alkyl group.
 3. The compound of claim 1 wherein Z comprises a divalent oligomeric ester radical, said radical having the structure:

wherein: R₁₁ and R₁₂ are independently selected from H or C₁-C₁₀ alkyl groups; n comprises an integer between 1 and 10; and m comprises any positive integer or fraction between 1 and
 20. 4. The compound of claim 2 wherein Z comprises a divalent oligomeric ester radical, said radical having the structure:

wherein: R₁₁ and R₁₂ are independently selected from H or C₁-C₁₀ alkyl groups; n comprises an integer between 1 and 10; and m comprises any positive integer or fraction between 1 and
 20. 5-8. (canceled)
 9. A composition comprising: a) an organic material which is subject to oxidative, thermal or light-induced degradation, and b) at least one compound of formula:

wherein: R₁-R₈ are independently selected from the group consisting of: H, F, Cl, Br, I, C₁-C₂₀ alkyls, C₁-C₂₀ cycloalkyls, C₁-C₂₀ alkoxy groups, C₇-C₂₀ phenylalkyls, and phenyl groups; A comprises a C₂-C₂₀ alkyl group or a divalent oligomeric oxyalkylene radical; Z comprises a C₂-C₂₀ alkyl or a divalent oligomeric ester radical; and G comprises an end group selected from the group consisting of: H, C₁-C₁₀ alkyls, alkyl carbonyls and aryl carbonyls.
 10. The composition of claim 9 wherein A comprises a divalent oligomeric oxyalkylene radical having the structure:

wherein: EO comprises ethylene oxide or a derivative thereof; PO comprises propylene oxide or a derivative thereof; R₉ comprises a divalent C₁-C₂₀ alkyl radical; x, y and w are independently selected from the group consisting of: zero and positive integers or fractions between 1 and 20; the sum of x+y+w is equal or greater than 1; and R₁₀ comprises H or a C₁-C₂₀ alkyl group.
 11. The composition of claim 9 wherein Z comprises a divalent oligomeric ester radical, said radical having the structure:

wherein: R₁₁ and R₁₂ are independently selected from the group consisting of: H and C₁-C₁₀ alkyl groups; n comprises an integer between 1 and 10; and m comprises any positive integer or fraction between 1 and
 20. 12. The composition of claim 9 wherein said organic material comprises a synthetic polymer. 